SL-250 Double-liquid type PU quick leak stopage agent

1. No-shrink 2. Dry out quickly 3.High strength 4.Low viscosity 5.Resist to acid and alkali,etc.

SL-250 Double-liquid type PU quick leak stopage agent

Product feature

1. No shrink after hardening.

2. Low viscosity. Below 300cps, material can completely infiltrate into Micro-crack. It has double water-stop and reinforcement effects

3. It can be harden in water. This material can be applied to wet surface.

4. Fast setting. After mixing, the mixture will react in 10 seconds. it can dry out completely in 30 seconds, and dry out completely in 1 minute.

5. After mixing, pressure strength for the mixture is around 4000psi

6. High strength, wear resistant, Strength resistance, Impact resistance, puncture strength up to 140KG+

7. Resist to acid and alkali, anti-corrosion, Oil Resistance, no peeling, not cracking

8. Completely watertight, low water absorption, fine texture, no bubble after hardening

9. No harmful metals as lead, mercury, Cadmium, etc. no cyanide and chloride, harmless

Construction location

Anti-leakage, waterproofing, reinforce the enclosure wall of basement, the cracks of the ceiling, bottom. Treat damaged wall, fight water pressure beam structure, strengthen and surface waterproofing, reinforce the anti-leakage of cracks, holes.

Method of use

Clean construction surface, directly spray solution on construction surface for 2-3 times, when spraying the second time it is necessary to wait until the first spraying time dries out completely. When reinforcing/anti-leakage/waterproofing it is necessary to coordinate to use SL-600 machine. 

 

Applicable Tools

1. A set of two components high pressure grout machine

2. Two sets of one component high pressure grout machine with dual fluid switch

 

3. Use roller, brush or spray machine to paint and spray

  

Test report

Test item	Test result	Test method
Response Time(begin to heat)	10sec	Hand touch
Solidification complete	80sec	CNS 785
Viscosity	200~300cps	CNS 5607
Bonding Strength	More than 27kgf/cm²	CNS 12611
Water absorption	Less than 0.4%	ASTM D570
Hardness	D63/s	ASTM D2240
Puncture strength	More than 140 kgf/cm²	ASTM E154
Compressive strength	More than 300kgf/cm²	ASTM C109
Bending strength	More than 290kgf/cm²	ASTM C348
Tensile strength	More than 290kgf/cm²	CNS 8645
Harden in water	Less than10 min	Hand touch
Wet surface Bonding Strength	More than 10 kgf/cm²	CNS 8683
Acid and alkali resistance (5%)	pass	CNS 4447

   